As promising heavy metal-free emitting materials, Ag-In-Se nanocrystals (NCs) are conventionally synthesized using organic phosphine agents and exhibit near-infrared emissions. In this work, we demonstrate a rapid phosphine-free approach for synthesizing Ag-In-Se alloy NCs with the emissions tunable to the visible region on the basis of the phosphine-free dissolution of Se powder. At room temperature, Se powder is reduced by dodecanethiol and dissolved in oleylamine to produce a Se precursor. The resultant Se precursor is highly active, which permits rapid synthesis at a relatively low temperature, such as at 90 degrees C for 150 s. By optimizing the size, structure, and composition, the photoluminescence quantum yield of the as-synthesized Ag-In-Se NCs is enhanced to up to 10%. The growth of the Ag-In-Se NCs involves composition and phase transition, which strongly depend on the reaction temperature. The Ag2Se nuclei form first, and the Ag-In-Se NCs are produced by doping In3+ into the preformed Ag2Se nuclei. Tetragonal phase Ag-In-Se is obtained below 170 degrees C, while the orthorhombic phase appears over 190 degrees C. The potential of Ag-In-Se NCs as red emitting phosphors for lighting-emitting diodes is further demonstrated.
[1]Jilin Univ, Coll Chem, State Key Lab Supramol Struct & Mat, Changchun 130012, Peoples R China.
[2]Harbin Med Univ, Affiliated Hosp 1, Dept Dermatol, Harbin 150001, Peoples R China.
[3]Jilin Univ, Hosp 1, Dept Hand & Foot Surg, Changchun 130021, Peoples R China.
(8.0+极速模式)